HS Code |
707059 |
| Polymer Type | Chloroprene Rubber (CR) |
| Grade | Baypren 210 |
| Appearance | Light colored chips |
| Mooney Viscosity Ml 1 4 100c | 40-50 |
| Specific Gravity | 1.23 |
| Volatility | <1% (at 105°C, 3h) |
| Ash Content | <0.7% |
| Tensile Strength | Above 20 MPa (typical for CR) |
| Elongation At Break | Above 600% (typical for CR) |
| Oil Resistance | Good |
| Ozone Resistance | Excellent |
| Processing | Easily processable, suitable for extrusion and molding |
| Colorability | Good |
| Storage Stability | At least 24 months under cool, dry conditions |
As an accredited Baypren 210 Chloroprene Rubber (CR) factory, we enforce strict quality protocols—every batch undergoes rigorous testing to ensure consistent efficacy and safety standards.
| Packing | Baypren 210 Chloroprene Rubber (CR) is packaged in 25 kg polyethylene-lined paper bags, labeled with product name, batch number, and manufacturer. |
| Storage | Baypren 210 Chloroprene Rubber (CR) should be stored in a cool, dry, and well-ventilated area, away from direct sunlight, heat sources, and moisture. The material should be kept in its original, tightly sealed packaging to prevent contamination. Avoid contact with oils, solvents, and strong oxidizing agents to maintain quality and prevent degradation. Store at recommended temperatures below 30°C. |
| Shipping | Baypren 210 Chloroprene Rubber (CR) is typically shipped in moisture-proof, 25 kg polyethylene-lined paper bags or bulk containers. The material should be stored and transported in a cool, dry place, away from direct sunlight and incompatible chemicals, ensuring bags remain sealed to prevent contamination and moisture absorption during transit. |
Competitive Baypren 210 Chloroprene Rubber (CR) prices that fit your budget—flexible terms and customized quotes for every order.
For samples, pricing, or more information, please contact us at +8615365186327 or mail to sales3@ascent-chem.com.
We will respond to you as soon as possible.
Tel: +8615365186327
Email: sales3@ascent-chem.com