| Product Name | LUMISIL 100 OD A/B Silicone Rubber |
| Type | Addition-cure silicone rubber |
| Mix Ratio | 1:1 (A:B by weight) |
| Appearance | Translucent |
| Hardness Shore A | A 10 (approximate) |
| Pot Life | 60-90 minutes at 23°C |
| Cure Time | 8-24 hours at room temperature |
| Viscosity | Low (pourable) |
| Tensile Strength | 2.5 MPa (approximate) |
| Elongation At Break | 300% (approximate) |
| Tear Strength | 6 kN/m (approximate) |
| Service Temperature Range | -50°C to 200°C |
| Density | 1.05 g/cm³ |
| Colorability | Can be colored with silicone pigments |
| Uses | Mold making, encapsulation, prototyping |
As an accredited LUMISIL 100 OD A/B Silicone Rubber factory, we enforce strict quality protocols—every batch undergoes rigorous testing to ensure consistent efficacy and safety standards.
| Packing | LUMISIL 100 OD A/B Silicone Rubber is packaged in two separate 1 kg containers, each clearly labeled A and B components. |
| Storage | LUMISIL 100 OD A/B Silicone Rubber should be stored in its original, tightly sealed containers at a temperature between 5°C and 25°C (41°F and 77°F), away from direct sunlight, moisture, and sources of ignition. Ensure the storage area is well-ventilated and dry. Avoid freezing and excessive heat to maintain product quality and prevent premature curing or degradation. |
| Shipping | LUMISIL 100 OD A/B Silicone Rubber is typically shipped in sealed containers, such as pails or drums, to ensure product integrity and prevent contamination. The packaging is clearly labeled with handling and hazard information. During transit, it must be protected from extreme temperatures and stored upright to avoid leakage or spillage. |
Competitive LUMISIL 100 OD A/B Silicone Rubber prices that fit your budget—flexible terms and customized quotes for every order.
For samples, pricing, or more information, please contact us at +8615365186327 or mail to sales3@ascent-chem.com.
We will respond to you as soon as possible.
Tel: +8615365186327
Email: sales3@ascent-chem.com