| Product Name | Rajshila HS-1281 Silicone Rubber |
| Type | High Strength Silicone Rubber |
| Appearance | Translucent or White |
| Hardness Shore A | 25-30 |
| Mixing Ratio | 10:1 (Base: Catalyst) |
| Pot Life | 30-40 minutes at 25°C |
| Curing Time | 3-5 hours at room temperature |
| Tensile Strength Mpa | 4.0-5.5 |
| Elongation At Break | 350-450% |
| Tear Strength Kn M | 15-20 |
| Operating Temperature Range | -55°C to +200°C |
| Viscosity Cp | 25000-35000 |
| Density G Cm3 | 1.08±0.05 |
| Shrinkage Percent | <0.3% |
| Color | White or Translucent |
As an accredited Rajshila HS-1281 Silicone Rubber factory, we enforce strict quality protocols—every batch undergoes rigorous testing to ensure consistent efficacy and safety standards.
| Packing | The Rajshila HS-1281 Silicone Rubber is packaged in a sturdy 20 kg metal drum, featuring clear product labeling and handling instructions. |
| Storage | Rajshila HS-1281 Silicone Rubber should be stored in tightly sealed original containers, away from direct sunlight, moisture, and sources of heat. Keep in a cool, dry, and well-ventilated area at temperatures between 5°C and 30°C. Avoid contamination with dust or other chemicals. Proper storage ensures product stability and extends shelf life. Always follow manufacturer’s guidelines for safe handling. |
| Shipping | Rajshila HS-1281 Silicone Rubber is securely packaged in sealed containers to prevent contamination and ensure safe transit. Shipping is conducted in accordance with industry safety standards and regulations. The product is clearly labelled, stored in cool, dry conditions, and handled to avoid exposure to extreme temperatures, moisture, or physical damage. |
Competitive Rajshila HS-1281 Silicone Rubber prices that fit your budget—flexible terms and customized quotes for every order.
For samples, pricing, or more information, please contact us at +8615365186327 or mail to sales3@ascent-chem.com.
We will respond to you as soon as possible.
Tel: +8615365186327
Email: sales3@ascent-chem.com