| Brand | Rajshila |
| Product Name | HS-3451 Silicone Rubber |
| Type | Addition Cure Silicone Rubber |
| Color | Translucent |
| Hardness Shore A | 40-45 |
| Mixing Ratio | 1:1 (Base to Catalyst) |
| Pot Life | 30-40 minutes |
| Curing Time | 4-6 hours at room temperature |
| Tensile Strength | 4.5 MPa |
| Elongation At Break | 400% |
| Viscosity | 24000-26000 cP |
| Density | 1.10 ± 0.05 g/cm³ |
| Tear Strength | 18 N/mm |
| Operating Temperature Range | -50°C to 200°C |
| Storage Conditions | Cool, dry place below 30°C |
As an accredited Rajshila HS-3451 Silicone Rubber factory, we enforce strict quality protocols—every batch undergoes rigorous testing to ensure consistent efficacy and safety standards.
| Packing | The Rajshila HS-3451 Silicone Rubber is packaged in a 20 kg blue drum with clear labeling and safety instructions printed. |
| Storage | Rajshila HS-3451 Silicone Rubber should be stored in a cool, dry, and well-ventilated area, away from direct sunlight, heat sources, and moisture. Keep containers tightly closed when not in use. Avoid contamination with other materials and store away from strong acids, alkalis, and oxidizing agents. Ideal storage temperature is typically between 5°C and 30°C to maintain product stability. |
| Shipping | Shipping for *Rajshila HS-3451 Silicone Rubber* is conducted in sealed, moisture-proof containers to prevent contamination and ensure product integrity. The chemical should be transported upright, securely fastened, and protected from extreme temperatures. Compliance with local and international regulations for industrial chemical shipping is required. Store in cool, ventilated conditions away from direct sunlight. |
Competitive Rajshila HS-3451 Silicone Rubber prices that fit your budget—flexible terms and customized quotes for every order.
For samples, pricing, or more information, please contact us at +8615365186327 or mail to sales3@ascent-chem.com.
We will respond to you as soon as possible.
Tel: +8615365186327
Email: sales3@ascent-chem.com